Method for separating trivalent americium from trivalent curium

ABSTRACT

The invention relates to a method for separating trivalent americium from trivalent curium. According to the inventive method, an aqueous solution containing at least said cations is contacted, at an acid concentration of 0.01 mol/L to 1 mol/L, with an organic solvent containing a bis(aryl)dithiophosphinic acid of general formula (4), wherein R 1 =phenyl- or naphthyl, R 2 =phenyl- or naphthyl, with methyl-, ethyl-, propyl-, isopropyl-, cyano-, nitro-, halogenyl-(Cl − , F − , Br − , J − ) substituted radicals of R 1  and R 2 , R 1  and R 2  being optionally substituted by at least one component from the group comprising methyl-, ethyl-, propyl-, isopropyl-, cyano-, nitro-, halogenyl-(Cl − , F − , Br − , J − ), and with a synergist of general formula (5), wherein X and/or Y and/or Z=RO (=alkoxy) or R (=alkyl), R being optionally branched and/or unbranched. The separation factor for americium (III) and curium (III) has an order of magnitude of 10.

The invention relates to a method of separating trivalent americium form trivalent curium in accordance with the preamble of claim 1.

The separation of trivalent actinides like americium (Am) or curium (Cu) from trivalent lanthanides has been a problem for a long time. The difficulties derive from the fact that the elements to be separated are very similar chemically and the trivalent ions of lanthanides and actinides also have similar physical properties. Especially the very similar ionic radii contribute to similar properties of both element groups. Thus a large number of investigations have already been carried out to attempt to separate with the highest possible selectivity and high efficiency the trivalent ions of actinides and lanthanides.

It is indeed known that extraction agents with soft donor groups, which contain nitrogen or sulfur as complex-forming structural components have a certain selectivity in liquid-liquid extraction with respect to trivalent actinides but can carry out the separation hitherto only at relatively high pH values at which the trivalent actinides tend toward precipitate formation.

In accordance with the publication K. L. Nash, Solvent Extraction, Ion Exchange. 11(4), 729-768 (1993), the known Talspeak Process is a selective extraction of lanthanides with the aid of complexing agents which hold the trivalent actinides in solution. However, this separation process also requires relatively high pH values of 3 to 4 and requires the addition of further salts.

A process available from the Applicant for the extraction of trivalent actinides from aqueous solutions which contain trivalent actinides and trivalent lanthanides which enable a separation at high acid concentrations of 0.01 to 2 mol/l HNO₃ (EP 1 019 552 B1) in accordance with this process, such an acid aqueous solution which contains a mixture of trivalent lanthanides and actinides, is extracted by means of an organic solvent which contains as the extraction agent, a bis (aryl)dithiophosphinic acid to which a synergist is added. With this method, because of the low pH value or high acid concentration, a precipitation of the trivalent actinides is limited and especially good separation results are obtainable. To evaluate the separation effect, the distribution coefficient D and the separation factor SF are considered. D _(AN(III)) =[AN(III)_(org) ]/[An(III)w]  (1)

In formula 1:

-   -   D_(AN(III))=The distribution Coefficient for Trivalent Actinide         (dimensionless)     -   [AN(III)_(org)]=Connection of the Trivalent Actinide in the         Organic Phase (mol/l)     -   [An (III)w]/=Concentration of the trivalant actinide in the         aqueous phase of mol/liter).         D _(LN(III)) =[Ln(III)_(org) ]/[Ln(III)_(w)}]  (2)

In formula 2:

-   -   D_(LN(III))=Distribution Coefficient for a trivalent lanthanide         (dimensionless)     -   [Ln(III)_(org)]=Concentration of the trivalent lanthanide in the         organic phase (mol/liter)     -   [Ln(III)_(w)}]=The concentration of the trivalent lanthanide in         the aqueous phase (mol/liter)         SF=D _(AN(III)) /D _(LN(III))   (3)

SF=Separation Factor (Dimensionless)

With a separation factor of SF=1, no separation is possible.

In accordance with that process using bis(aryl)dithiophosphine acid in strongly acid medium, the separation factor SF between trivalent actinides and trivalent lanthanides, depending upon the synergist, lies between 20 and 2000.

There exist various methods for the separation of the trivalent actinides (An) (III) Am and Cm from highly active liquid wastes, the Raffinate of the Purex Process. Madic, C. In 6^(th) Information Exchange Meeting on Actinide and Fission Product Partitioning and Transmutation, Madrid, Spain, 11-13 Dec. 2000, EUR., 19783, 2001, S. 53 to 64.

In the first step the An III are coextracted together with the lanthanides Ln(3) and the greater part of the fission products (for example Mo, Zr, Cs, Fe, etc. are separated out. The TRUEX, TRPO and the DIAMEX-processes belong to those known processes in all of the these processes (An/III)/Ln(III) such fractions are obtained that require further separation, hitherto with considerable problems. Up to know there has been no extraction agent which can selectively separate An(III) from Ln(III) of strongly acidic solutions. If one thinks of the P & T Nuclear Fuel Circulation in which the long lived actinides are first separated off (Partitioning, P) and then eliminated by transmution T, a An(III)/Ln(III)—separation is impermissible on the following grounds.

About a third of the fission products are lanthanides.

The Ln(III) have the same oxidation state (III) as the An(III) and the chemical characteristics are very similar to those of the AnIII.

Several lanthanides have very large neutron capture cross sections and act as neutron poisons with respect to the transmutation.

In the DIAMEX-Process, the An(III) and Ln(III) are extracted together from the 3 to 4 mol/L HNO₃ containing Purex-Raffinate with the aid of melanic acid diamide. After the back extraction with dilute HNO₃, one obtains a product which is comprised primarily of the An(III) and Ln(III) as well as an HNO₃ concentration of about 0.5 mol/liter (Madic, C.; Hudson, M. J.; Liljenzin, J. O.; Glatz, J. P.; Nannicini, R.; Facchini, A.; Kolarik, Z.; Odoj, R. New partitioning techniques for minor actinides, European report, EUR19149, 2000).

The present Applicant has also developed a method for actinide-lanthanide separation from nitric acid solutions (0.5 to 1.0 mol/liter HNO₃) this process is known under the name ALINA for (Actinide (III)-Lanthanide(III) Intergroup separation in Acidic Medium). (Modolo, G.; Odoj, R.; Baron, P. The ALINA Process for An(III)/Ln(III) Group Separation from strong Acidic Medium, Proceedings of Global 99, International Conference on Future Nuclear Systems, Jackson Hole, Wyo., USA, Aug. 29-Sep. 3, 1999; American Nuclear Society, Inc.).

As the extraction agent a mixture of aromatic dithiophosphinic acid and trioctylphosphinic oxide (TOPO) in tertiary butyl benzene is used. Details for the synthesis of the new extraction agent, its radiolitic stability and its suitability for AN(III)/Ln(III) separation are disclosed in (Modolo, G.; Odoj, R. Synergistic selective extraction of actinides (III) over lanthanides form nitric acid using new aromatic diorganyldithiophosphinic acids and neutral organophosphorus compounds. Solvent Extr. Ion Exch. 1999m 17 (1), S. (33-53).

The separation of Americium and Curium is however still more difficult than Actinide (III)-/Lanthanide (III) separation and has even greater requirements or process chemistry for the following reasons:

In the trivalent state, Americium and Curium have very similar chemical properties based upon their practically identical ionic radii (0.99 or 0.986 Angstrom). Americium is found in its higher oxidation states (IV, V, VI) as a very strong oxidizing agent and the nonhydrometallurgical (liquid-liquid extraction) for example the PUREX process) do not always allow separation of the heterovalent actinide because of the instability of all oxidation states up to the trivalent oxidation state. For that reason the structure does not describe any hydrometallurgical rocess which can separate americium and curium form one another in their natural oxidation states.

It is therefore the object of the invention to provide a method of separating americium and curium which has an especially high separation factor SF. The new method should also be readily integratable or includable in already known processes for lanthanide-actinide separation.

Starting from the preamble of claim 1, the objects are achieved according to the invention by the features given by the characterizing part of claim 1.

With the method of the invention it is possible directly to separate Americium (III) and Curium (III) with a separation factor of the order of magnitude of 10. It enables apart from Americium (III)/Curium (III) separation also an actinide (III)/lanthanide(III) separation.

Advantageous features of the invention are given in the dependent claims. The figures show by way of example schematic process modes.

They show:

FIG. 1: A diagram of a separation process according to the invention for Americium (III) and Curium (III) connected to a PUREX-process.

FIG. 2: a diagram of a process made in which the two cations Americium (III) and Curium (III) are initially removed together from a lanthanide solution and then the Americium (III) is separated from the Curium (III).

According to the method of the invention, the ions of Americium (III) and Curium (III) are separated in an aqueous phase. The solution can then also contain other lanthanides or actinides as well as their components.

For this purpose the aqueous solution containing Americium III and Curium (III) is brought into contact with an organic phase which contains an extraction agent and synergist. As the organic solvent, various systems come into consideration. Thus, a pure solvent as well as solvent mixtures containing at least two solvent components can be used.

Among the solvents which can be used are aromatic solvents, especially those aromatic solvents which are liquid at room temperature like benzol, toluene, tertiary butylbenzol, xylon, xylene, bis or tris-(isopropyl)benzene alone or in mixtures of at least two of these components.

Also can be used branched and/or unbranched aliphatic solvents having a chain length of, for example, C₅ to C₁₄ and generally room temperature liquid aliphatic solvents alone or in mixtures. Especially n-hexane, c-hexane, haptane, octane, nonane, decane, dodecane, kerosone or TPN must merit cancellation.

Preferably is the solvent a mixture of aromatic and aliphatic solvents is used, especially preferably an aromatic solvent, particularly especially preferably as the aromatic component that is greater than 50%.

As solvent, for example, toluene, hexane, a mixture of iso octane and tertiary butylbenzol can be named. The organic solvent is advantageously a solvent containing aromatic component, like benzene, toluene, zylene, tertiary benzene, or a pure automatic solvent.

In one mode of the invention the solvent used has at least one component from the group of benzol, toluene, xylol, tertiary butylbenzol and bis or tris tertiary butyl benzene and bis or tris isopropyl benzene. The use of a solvent has an additional positive effect in that it additional improves the distribution coefficients of the actinide Am(III) and Cm(III). The separation factor remains constant at about 10.

The sequence of the solvent effectiveness for the distribution coefficients is as follows:

Benzol<Toluene<Xylene<tertiary butyl benzene less than n-hexane/toluene (50/50, Table 4) bis-(isopropyl)benzene, triisopropylbenzene, bis-(tertiary butyl benzene), tris-tertiary tributyl benzene.

The extraction agents which are in the organic phase can preferably include an automatic dithiophosphinic acid, preferably (chlorophenyl)dithiophosphinic acid.

The extraction is carried out generally by means of an organic solvent which contains an extraction agent in the form of a bis(aryl)dithiophosphinic acid the general formula (4) R₂PS(SH)

with R₁=phenyl or naphthyl,

R₂=phenyl or naphthyl,

as well as methyl, ethyl, propyl, isopropyl, cvyano, nitro, halogenyl, (Cl—, F—, Br—, J-) substituted residues of R₁ and R₂ whereby R₁ and R₂ can be substituted with at least one component from the group of methyl ethyl isopropyl, cyano, nitro, halogenyl (Cl—, F—, Br—, J-). These groups are for example substituents which increase the acidity of the extraction agent bis(aryl)dithiophosphine acid which give rise to especially good extraction results. Decisive is the increase of the acidity of the extraction agent. The exact positions of the substituents is less significant.

The synergist which is introduced into the organic phase is preferably a trialkylphosphate (Formula (5)) with X, Y, Z=RO, preferably tris(ethylhexyl)phosphate (TEHP) or a trialkyl phosphinic oxide with X, Y, Z=R like for example trioctyl phosphinic oxide (TOPO).

With X and/or Y and/or Z=RO (alkoxy) or R(alkyl), R can be branched or unbranched and preferably is C4-C10 alkyl. All residues X, Y, Z can be R or RO. However, it is possible that, depending upon the case, only one or two of X, Y, Z will be RO or R.

Especially preferably the organic phase contains at least one synergist from the group comprised of trioctylphosphate (Formula 6)), tris-(2-ethylhexyl)-phosphate (Formula 7) and tris-(2-propylpentyl)-phosphate (Formula (8)). (CH₃CH₂CH₂CH₂CH₂CH₂CH₂CH₂—O—)₃P═O CH₂CH₃   (6) (CH₃CH₂CH₂CH₂CH₂CH₂—O—)₃P═O CH₂CH₃CH₃   (7) (CH₃CH₂CH₂CH₂CH₂—O—)₃P═O   (8)

With the addition of the synergist according to the invention there is a significant increase in the separation factor SF.

The selectivity in the separation of Am(III) from Cm(III) is significantly increased. The separation of Am(III) from Cm(III) is carried out at an acid concentration which is dependent upon the materials and material properties and concentration of the extraction arrangement, the synergist and the solvent The conditions must be so selected that the distribution coefficient of Am(III) is greater than 1 and the distribution coefficient for Cm(III) as a consequence is smaller than 1. Examples of possible acid concentrations for two different solvents for 0.5 mol/liter (ClPh)₂PSSH+0.15 mol/L TEHP are given in Table 4. The H⁺ concentrations can lie between 0.01-1 mol/liter for the separation according to the invention. Preferred is a range between 0.05 and 0.5 mol/liter. As acids, especially Hcl, H₂SO₄ can be used by way of example and especially HNO₃ is used since HNO₃ forms easily soluble salts. With this procedure according to the invention, Am(III) can be separated from Cm(III) both from a solution containing these components alone as well as from a solution which contains additional ions or cations like for example alkyl elements, alkaline earth elements, althanides(III) and lanthanides (IV, V, VI).

In the extraction experiments with dithiophosphinic acid for actinide (III)/lanthanide III separation in accordance with the state of the art, up to now it has been found that Americium (III) and Curium(III) have similar properties and the same extraction characteristics, that is similar distribution coefficients and thus SP_(Am/Cm−1). As a result curium(III) was not heretofore considered. The results of the extraction experiments with Curium(III) have shown, astonishingly, a difference in the properties for the first actinide elements. The extraction experiments according to the invention carried out with synthetic actinide(III)/Lanthanide(III) solutions use the compositions in Table 1. These actinide(III)/lanthanide(III) solutions arise in a DIAMEX process for actinide(III) separation from a PUREX raffinate. TABLE 1 Composition of Concentrated Actinide(III)/Lanthanide(III) solutions from a DIAMEX process traced with Am-241 and Cm-244. The concentrations of the Lanthanides(III) correspond to 2.5 or ten times the expected concentrations. As a result, KF = 2.5 and 10. KF* = 2.5 KF = 10 ELEMENT (MG/L) (MG/L) Am Trace Amount Trace Amount Cm Trace Amount Trace Amount Y 229 929 La 670 3032 Ce 1340 5926 Pr 640 2690 Nd 2476 10261 Sm 469 1902 Eu 90 367 Gd 117 448 *KF = Concentration Factor

The results of extraction experiments are shown in Tables 2 and 3. One can see that the distribution coefficient of Y, Nd, Sm, Eu and Gd are significantly smaller than those of La, Ce and Pr.

Ce is the best extracted Lanthanide. As a consequence, for example, the Am/Eu separation factor is very high (SF_(Am/Eu)>1000), but for example the Am/Ce separation factor is only moderate (SF_(Am/Ce)=25-40) for continuous An(III)/Ln(III), this separation factor is more than sufficient. Since however the distribution coefficient of the Cm is smaller by a factor of 10 than that of the Am, (SF_(Am/Ce)) a separation of Cm is also possible.

The results in Table 3 clearly show that with the extraction system (ClPh)₂PSSH+TEHP, concentrated An/Ln solutions (KF=10) can be handled. The comparison with the values in Table 2 show that indeed the distribution coefficients of all elements under the same conditions are somewhat smaller but the separation factors SF_(Am/Eu), SF_(Am/Ce), SF_(Cm/Eu) and SF_(Cm/Ce) increase. To be noted are the higher Am/Eu and Am/Gd separation factors of over 2000. The Am/Ce separation factor is 2 orders of magnitude smaller and is 36 to 40. The Am/Cm separation factor is also here about 10. At this point it may be noted that in the literature up to now no separation factor has been cited. Up to now only values below 2 are known. TABLE 2 Extraction of Am(III), Cm(III) and lanthanides (III) with 0.4 mole/liter (ClPh)₂PSSH and 0.15 mole per liter TEHP in 20% iso- octane/tertiary butylbenzene from a synthetic An(III)/Ln(III) solution. Organic Phase: 0.4 mole per liter (ClPh)₂PSSH plus 0.15 mole per liter TEHP in 20% iso-octane tertiary butylbenzene. Aqueous Phase: Synthetics An(III), Cm(III) Solution with the composition in Table 1 (KF = 2.5) with various HNO₃ concentrations: [HNO₃] 0.1 0.2 0.3 0.5 1.0 Distribution Coefficient D Am-241 13.65 3.68 0.83 0.14 0.013 Cm-244 1.20 0.27 0.084 0.016 0.0025 Y 0.0071 0.0013 0.0005 0.0001 0.0000 La 0.42 0.093 0.019 0.0034 0.0003 Ce 0.58 0.13 0.033 0.0046 0.0004 Pr 0.29 0.064 0.013 0.0024 0.0002 Nd 0.079 0.0067 0.0017 0.0006 0.0001 Sm 0.017 0.0029 0.0010 0.0002 0.0000 Eu-152 0.011 0.0019 0.0008 — — Eu 0.012 0.0021 0.0007 0.0002 0.0000 Gd 0.071 0.016 0.0043 0.0008 0.0001 Separation Factor SF SF_(Am/Eu) 1240.9 1752.4 1012.1 636.4 183.1 SF_(Am/Ce) 23.5 28.3 25.2 30.4 29.5 SF_(Am/Cm) 11.4 13.6 9.9 8.7 5.2 SF_(Cm/Eu) 109.1 142.1 102.4 72.7 35.2 SF_(Cm/Ce) 2.1 2.1 2.5 3.5

TABLE 3 Extraction of Am(III), Cm(III) and lanthanides (III) with 0.4 mole/liter (ClPh)₂PSSH and 0.15 mole per liter TEHP in 20% iso- octane/tertiary butylbenzene from a synthetic An(III)/Ln(III) solution. Organic Phase: 0.4 mole per liter (ClPh)₂PSSH plus 0.15 mole per liter TEHP in 20% iso-octane tertiary butylbenzene. Aqueous Phase: Synthetics An(III), Cm(III) Solution with the composition in Table 1 (KF = 10) with various HNO₃ concentrations: [HNO₃] 0.1 0.2 0.3 0.5 1.0 Distribution Coefficient D Am-241 13.65 3.68 0.83 0.14 0.013 Cm-244 1.20 0.27 0.084 0.016 0.0025 Y 0.0071 0.0013 0.0005 0.0001 0.0000 La 0.42 0.093 0.019 0.0034 0.0003 Ce 0.58 0.13 0.033 0.0046 0.0004 Pr 0.29 0.064 0.013 0.0024 0.0002 Nd 0.079 0.0067 0.0017 0.0006 0.0001 Sm 0.017 0.0029 0.0010 0.0002 0.0000 Eu-152 0.011 0.0019 0.0008 — — Eu 0.012 0.0021 0.0007 0.0002 0.0000 Gd 0.071 0.016 0.0043 0.0008 0.0001 Separation Factor SF SF_(Am/Eu) 1240.9 1752.4 1012.1 636.4 183.1 SF_(Am/Ce) 23.5 28.3 25.2 30.4 29.5 SF_(Am/Cm) 11.4 13.6 9.9 8.7 5.2 SF_(Cm/Eu) 109.1 142.1 102.4 72.7 35.2 SF_(Cm/Ce) 2.1 2.1 2.5 3.5

In Table 4, several extraction results of the Am(III)/Cm(III) separation form nitric acid solution have been given.

The results show that the distribution coefficients are strongly dependent upon the solvent but the Am/Cm separation factor SF_(Am/Cm) is approximately unaffected. The distribution coefficients of Am and Cm (together in solution) are determined by alphaspectroscopy and the Am additionally by gamma spectroscopy. The alphaspectroscopy has the advantage that both nucleides (here Am-241 and Cm-244) can be simultaneously measured. TABLE 4 Extraction of Am(III)/Cm(III) with 0.5 mole per liter with ((ClPh)₂PSSH and 0.15 mole per liter TEHP depending upon the solvent. Organic Phase: 0.5 mole per liter (ClPh)₂PSSH plus 0.15 mole per liter Tris (ethylhexyl phosphate in various solvents. Aqueous Phase: Tracer accounts of Am-241 and Cm-244, various HNO3 concentrations. n-hexane/toluene (50/50 as solvent) Toluene as Solvent [HNO₃] D_(Am(α)) D_(Am(α)) D_(Cm(α)) SF_(Am(α))/_(Cm(α)) N-haxane/Toluene (50/50 as solvent) 0.1 133.697 155.50 16.2778 9.553 0.2 12.613 8.3936 1.0928 7.681 0.5 0.5538 0.2654 0.0286 9.289 1.0 0.0385 0.0175 0.0049 3.534 Toluene as Solvent 0.1 7.2381 10.333 0.9733 10.62 0.2 0.6721 0.7672 0.0850 9.024 0.5 0.0296 0.0201 0.0024 8.319 1.0 0.00255 0.0031 0.0008 3.683

The method of the invention can be applied as FIG. 1 illustrates to known separation processes. In FIG. 1, based upon a work up of burned out fuel elements for the separation of uranium and plutonium (neptunium) and the subsequent separation of the trivalent actinides americium and curium from the HAW (purex raffinate) has been shown, as a separation process can be schematically explained:

The burned out fuel elements can be fed to a PUREX process in which the U, PU and NP are removed. The highly effective liquid waste (HAW) is fed to a separation of the actinides III and lanthanides (III).

The separated actinides(III) and lanthanides(III) are then subjected to a selective actinide(III) separation which, for example, is carried out in accordance with the process according to European Patent 1019552. Following the process according to European Patent 1019552, in the aqueous phase (for example, trivalent ions of ions (Cer), (Ce), Praseodymium (Pr), Neodymium (Nd), Promethium (Pr), Samarium (Sm), Europium (Eu), Gadolinium (Gd), Terbium (Tb), Dysprosium (Dy), Holmium (Ho), Erbium (Er), Thulium (Tm), Ytterbium (Yb), Lutetium (Lu), as well as Lanthanum (La) and Yttrium (Y) or at least one component of this group and ions of the trivalent actinides like Americium (Am) and Curium (Cm) are contained. The aqueous phase has a low pH value which corresponds to an H+ concentration of a strong acid of 0.01 to 2 moles per liter. As the acid, HcL, H₂SO₄ and especially HNO₃ forms easily soluble salts. The extraction is carried out by means of an organic solvent which contains bis(aryl)dithiophosphinic acid and of the general formula (4) R₂PS(SH)

where R₁=phenyl or naphthyl and

R₂=phenyl nathphyl.

As well as methyl-, ethyl-, propyl-, isopropyl-, cyano-, nitro-, halogenyl-, (CL⁻, F⁻, Br⁻, J⁻) substituted residues of R₁ and R₂ can be substituted with at least one of the components from the group of methyl-, ethyl-, propyl-, isopropyl-, cyano-, nitro-, halogenyl-, (CL⁻, F⁻, Br⁻, J⁻). These groups are substituents which can cause an increase in the acidicity of the extraction agent bis(aryl)dithiophosphinic acid and leads to good extraction properties. The increased acidity of the extraction agent is decisive and the exact positions of the substituents are of less significance. For example, the organic phase contains at least one synergist from the group comprised of trioctyl phosphate (Formula 6), Tris-(2-ethylhexyl)-phosphate (Formula 7) and Tris-(2-propylpentyl)-phosphate (Formula 8). (CH₃CH₂CH₂CH₂CH₂CH₂CH₂CH₂—O—)₃P═O CH₂CH₃   (6) (CH₃CH₂CH₂CH₂CH₂CH₂—O—)₃P═O CH₂CH₃CH₃   (7) (CH₃CH₂CH₂CH₂CH₂—O—)₃P═O   (8)

However, also the synergists of the general formulas 5 can be used.

With the addition of synergists, a significant increase in the separation factor SF is achieved. The selectivity in the separation of the actinides from the lanthanides is significantly increased.

The organic solvent is advantageously an aromatic component like benzene containing solvent or a pure aromatic solvent. In an especially advantageous feature of the invention, the solvent includes at least one group of Toluene, Xylene, Tertiary Butylbenzene, Propylene or Isopropylbenzene, bis or tris benzene. The use of a solvent has two additional positive effects:

Firstly, the selectivity of the An³⁺ extraction is further advanced. The other is that the distribution coefficient _(Dan)(III) is additionally improved.

The effect on the separation factor SF and the distribution coefficient follows the series: Benzene, Toluene, Xylene, Tertiary Butylbenzene, Bis-(isopropyl)-benzene, tri-isopropylbenzene, Tris-(tertiary butyl)-benzene.

In the following, the separation of Americium(III) and Curium(III) with the process of the invention is described.

A process according to the method of the invention has been given for example in FIG. 2.

FIG. 2 shows a separation utilizing the Luca process for actinide(III)/lanthanide(III) separation followed by Americium/Curium separation.

In this illustration the actinides (III) are extracted from an aqueous solution containing Americium(III) and Curium(III) as well as lanthanide (III) with 0.1 mole per liter HNO₃ using an extraction agent comprised of 0.4 mole per liter (ClPH)₂PSSH and 0.15 mole per liter and trisethylhexylphosphate in an organic phosphate. With a 0.3 mole per liter HNO₃ solution Curium(III) is then re-extracted. Thereafter follows the back extraction of Americium(III) with 1.0 mole per liter HNO₃.

The flow scheme is as follows:

1. Selective extraction of Americium and Curium. The lanthanides-Ln(III) here, Y, La, Ce, Pr, Nd, Sm, Eu and Gd remain in the raffinate (in the figure=Ln(III).

2. Selective stripping of Cm(III).

3. Stripping of Am(III). 

1. A method of separating trivalent Americium from trivalent Curium from an aqueous solution containing at least these cations, characterized in that the aqueous solution is contacted with an acid concentration of 0.01 mole per liter to 1 mole per liter with an organic solvent containing a bis(aryl)dithiophosphinic acid of the general formula (3) SF=D _(An(III)) /D _(Ln(III))   (3) with R₁=phenol or naphthyl R₂=phenol or naphthyl and substituted residues of R1 and R2 with methyl-, ethyl-, propyl-, isopropyl-, cyano-, nitro-, halogenyl-(Cl—, F—, Br—, J-) substituents and wherein R1 and R2 can be substituted by at least one component from the group of methyl-, ethyl-, propyl-, isopropyl-, cyano-, nitro-, halogenyl-(Cl—, F—, Br—, J-) as well as a synergist with the general formula (5)

with x and/or y and/or z=RO (alkoxy) or R (alkyl) whereby R can be branched and/or unbranched.
 2. The method according to claim 1 characterized in that the organic solvent is an aromatic solvent, an aliphatic solvent or a mixture thereof.
 3. The method according to claim 2 characterized in that, the aromatic solvent comprises at least one component from the group consisting of benzene, toluene, tertiary butylbenzene, xylene, bis or tris (tertiary butyl)benzene, isopropyl benzene bis/tris benzene.
 4. The method according to claim 2 characterized in that the aliphatic solvent is at least one component from the group of branched or unbranched aliphatic solvents with a chain length of C4 to C14.
 5. The method according to one of claims 2 or 4 characterized in that the aliphatic solvent is at least one component from the group comprised of n-hexane, c-hexane, heptane, octane, nonane, decane, undecane, dodecane, kerasine or TPH.
 6. The method according to one of claims 1 to 5 characterized in that the aromatic solvent is used as the main component.
 7. The method according to one of claims 1 to 6 characterized in that it follows a lanthanide-actinide separation process.
 8. The method according to claim 7 characterized in that the lanthanide-actinide separation process is a Talspeak, Truex, TRPO or Diamex process.
 9. The method according to claim 7 characterized in that the lanthanide-actinide separation process is a process in which the actinides are removed from an aqueous solution by means of a solvent containing a bis(aryl)dithiophosphinic acid of the general formula (4)

with R1=phenyl or naphthyl, R2=phenyl or naphthyl or the residues R1 and R2 substituted with methyl-, ethyl-, propyl-, isopropyl-, cyano-, nitro-, halogenyl-(Cl—, F—, Br—,J-), whereby R1 and R2 can be substituted with at least one of the components of the group of methyl-, ethyl-, propyl-, isopropyl-, cyano-, nitro-, halogenyl-(Cl—, F—, Br—,J-) as well as a synergist of the general formula (5)

with x and/or y and/or z=RO (=alkoxy), and/or R(=alkyl), whereby R is branched and/or unbranched. 